corrosion fatigue

基本解释

The transition conditions from corrosion fatigue to SCC have been discussed in terms of the cycling thermal stress and its stress ratio.
在本文中，从循环热应力及其应力比的角度，讨论了从腐蚀疲劳向应力腐蚀断裂过渡的条件。
Corrosion fatigue damage of concrete is the coupling action result of corrosion medium and load fatigue, and the study on this has been in the stage of theory search.
混凝土腐蚀疲劳破坏是腐蚀介质与交变荷载耦合作用的结果，对其研究目前国内外还仅处于理论探索阶段。
To do Corrosion Fatigue tests and analyses of typical Components of aircraft, the Compilation of aircraft.
要进行飞机典型构件的腐蚀疲劳试验和分析，就必须编制飞机载荷-环境谱。
hkxb.buaa.edu.cn

Even if corrosion, metal fatigue and parts obsolescence were not taking a toll on the planes, potential adversaries are buying better and better air defenses that will make it harder for the bombers to reach their targets in future wars.
FORBES: Air Force Wants A Bomber That Balances Cost With Capability

腐蚀疲劳
The failure of blower wheel is caused by corrosion fatigue with the analysis of material, macro and micro fracture appearance, and composition of corrosion material. The crack initiated from the corrosion pits.
通过材质、断口宏微观和腐蚀产物成分分析，确定鼓风机转子叶轮失效模式为腐蚀疲劳，鼓风机转子叶轮上裂纹起源于腐蚀坑。
航空、航天科学技术
腐蚀疲劳
The cumulative corrosion fatigue life model was established and its accuracy was verified. Corrosion damage characterization factors and the cumulative fatigue life attenuation function were taken as specimen.
定义了腐蚀疲劳寿命累积衰减函数与疲劳寿命衰减速率函数,建立了寿命累积衰减模型,验证了该模型的准确性,并以腐蚀损伤表征因子和腐蚀累积衰减函数为数据样本,用BP神经网络、自适应滤波的LMS算法分别预测了不同年限下的疲劳寿命。
交通运输工程
锈蚀疲劳
In this paper, the environment erosion and the fatigue damage are contraposed, the corrosion fatigue damages of the pile foundation in railway bridges under the disadvantageous factors are studied and explored.
本文针对钢筋混凝土桥梁中普遍存在的环境侵蚀和疲劳问题,研究与探讨了两不利因素共同作用下铁路桥梁桩基础的锈蚀疲劳损伤。
腐蚀疲劳