crushing strength

基本解释

• [力] 压碎强度；抗碎强度；破碎强度

英汉例句

双语例句

• The influence of green ball quality and palletizing crushing strength are studied by using different size distribution of DAYE concentrate.
  研究了不同的粒度组成大冶铁精矿对生球质量与成品球团抗压强度的影响。
• In addition, according to the crushing strength and physical, chemical properties of manganese nodule, the testing method for crushing using toothed roll crusher is established.
  同时根据锰结核的破碎强度和物理化学特性确定了用齿辊破碎方式进行破碎的实验方法。
• The bulk crushing strength and Abrasion strength are evidently different with the category of activated carbon.
  测定了原粒度活性炭的堆积压碎强度和磨耗强度。

权威例句

• Not only does the robot look Terminator-esque, but it's been designed to mimic the muscle system of a human (with bone-crushing strength, of course) and will be programmed with a semi-autonomous AI so that the android can learn new tasks, all of which is just a little too much like the Terminator for our comfort.
  ENGADGET: Prepare to be terminated: The Kibertron

• crushing strength更多例句

词组短语

短语

• crushing g strength 破碎强度
• increase particle crushing strength 提高强度
• crushing strength constant 压溃强度系数
• radial crushing strength test 径向压溃强度试验
• radial crushing strength constant 径向压碎强度系数

• crushing strength更多词组

专业释义

机械工程

• 压碎强度

  The porosity(Pa)was 36.97%,water absorption(Wa)was 20.34%,bulk density(D)was 1.82kg/m~3,crushing strength was 13.50MPa,acid resistance was 96.76%and alkali resistance was 97.38%,when the optimal sample YC2 was fired at 1080℃with 20 wt%additional content of graphite added.
  典型配方YC2石墨添加量达20wt%(外加),于1080℃下烧成样品的显气孔率为36.97%,吸水率为20.34%,体积密度为1.82kg/m~3,抗压碎强度为13.50MPa,耐酸性为96.76%,耐碱性为97.38%。

  化学

• 耐压强度

  By reducing the addition of reused magnesia chrome bricks,the crushing strength,MOR and bulk density became higher after drying and firing at medium and high temperature.
  随着废镁铬砖加入量的降低,烘干、中温和高温处理后的耐压强度、抗折强度、体积密度均逐渐增大。

  医药科学

• 抗碎强度

物理学

• 压碎强度
• 破碎强度
• 压毁强度
• 抗碎强度