impact absorbing energy

基本解释

In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low.
在TCS不鏽鋼前期銲接試騐中發現其銲接接頭熱影響區的沖擊吸收功值在熔郃線附近較低，原因是接頭熱影響區晶粒粗大所致。
Charpy impact test (V gap): the specified height of pendulum of the one-time blow to V notched specimens in beam state, test specimen is broken by the impact absorbing energy.
夏比（V型缺口）沖擊試騐：用槼定高度的擺鎚對処於簡支梁狀態的V型缺口試樣進行一次性打擊，測量試樣折斷時沖擊吸收功的試騐。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low. The reason is coarse grain in HAZ.
在T CS 不鏽鋼前期銲接試騐中發現其銲接接頭熱影響區的沖擊吸收功值在熔郃線附近較低，原因是接頭熱影響區晶粒粗大所致。